Influence of hot rolling modes  on grain-oriented silicon steel grain size

Metallurgy and materials technology. Mechanical engineering

Hot rolled grain-oriented silicon steel sheets microstructure behavior was investigated depending on rolling modes. During laboratory hot rolling reduction rate and initial rolling temperature were varied. Grain size and austenite volume fraction in deformed specimens was observed. Results of laboratory hot rolling were compared with real production hot rolling sheets.